Autoren: Maschke, Dominik G.
Titel: A new class of bragg stacks and its principle application
Online-Publikationsdatum: 29-Mai-2013
Erscheinungsdatum: 2013
Sprache des Dokuments: Englisch
Zusammenfassung/Abstract: This work is focused on the development of high quality nanoporous 1D photonic crystals –so called Bragg stacks – made by spin-coating of approximately 25 nm large SiO2 and TiO2 nanoparticles bearing interparticle voids large enough to infiltrate reactive species. Therefore, the first part of this work describes the synthesis of well-dispersed TiO2 nanoparticles in this size range (the corresponding SiO2 nanoparticles are commercially available). In the second part, a protocol was developed to prepare nanoporous Bragg stacks of up to 12 bilayers with high quality and precision. Tailor-made Bragg stacks were prepared for different applications such as (i) a surface emitting feedback laser with a FWHM of only 6 nm and (ii) an electrochromic device with absorption reversibly switchable by an external electrical bias independently of the Bragg reflection. In the last chapter, the approach to 1D photonic crystals is transferred to 1D phononic crystals. Contrast in the modulus is achieved by spin-coating SiO2 and PMMA as high and low moduli material. This system showed a band gap of fg = 12.6 GHz with a width of Dfg/fg = 4.5 GHz.
DDC-Sachgruppe: 000 Allgemeines
000 Generalities
Veröffentlichende Institution: Johannes Gutenberg-Universität Mainz
Organisationseinheit: FB 09 Chemie, Pharmazie u. Geowissensch.
Veröffentlichungsort: Mainz
URN: urn:nbn:de:hebis:77-32739
Version: Original work
Publikationstyp: Dissertation
Nutzungsrechte: Urheberrechtsschutz
Informationen zu den Nutzungsrechten:
Enthalten in den Sammlungen:JGU-Publikationen

Dateien zu dieser Ressource:
  Datei Beschreibung GrößeFormat
3273.pdf45.71 MBAdobe PDFÖffnen/Anzeigen