High quality colloidal crystals with different architectures and their optical properties

Abstract

In this present work high quality PMMA opals with different sphere sizes, silica opals from large size spheres, multilayer opals, and inverse opals were fabricated. Highly monodisperse PMMA spheres were synthesized by surfactant-free emulsion polymerization (polydispersity ~2%). Large-area and well-ordered PMMA crystalline films with a homogenous thickness were produced by the vertical deposition method using a drawing device. Optical experiments have confirmed the high quality of these PMMA photonic crystals, e.g., well resolved high-energy bands of the transmission and reflectance spectra of the opaline films were observed. For fabrication of high quality opaline photonic crystals from large silica spheres (diameter of 890 nm), self-assembled in patterned Si-substrates a novel technique has been developed, in which the crystallization was performed by using a drawing apparatus in combination with stirring. The achievements comprise a spatial selectivity of opal crystallization without special treatment of the wafer surface, the opal lattice was found to match the pattern precisely in width as well as depth, particularly an absence of cracks within the size of the trenches, and finally a good three-dimensional order of the opal lattice even in trenches with a complex confined geometry. Multilayer opals from opaline films with different sphere sizes or different materials were produced by sequential crystallization procedure. Studies of the transmission in triple-layer hetero-opal revealed that its optical properties cannot only be considered as the linear superposition of two independent photonic bandgaps. The remarkable interface effect is the narrowing of the transmission minima. Large-area, high-quality, and robust photonic opal replicas from silicate-based inorganic-organic hybrid polymers (ORMOCER® s) were prepared by using the template-directed method, in which a high quality PMMA opal template was infiltrated with a neat inorganic-organic ORMOCER® oligomer, which can be photopolymerized within the opaline voids leading to a fully-developed replica structure with a filling factor of nearly 100%. This opal replica is structurally homogeneous, thermally and mechanically stable and the large scale (cm2 size) replica films can be handled easily as free films with a pair of tweezers.